|  Brief introduction Kinds of grey and dipped tyre cord fabrics are made of polyester yarn. These grey and dipped polyester tyre cord fabrics are used as reinforcement for making radial tyres, light truck tyres, and other rubber products. Specification: We can supply polyester tyre cord fabrics of various specifications, grey or dipped such as 1000D/2, 1000D/3, 1300D/2, 1300D/3, 1500D/2, 1500D/3, 2000D/2, etc. Packing: Packed in rolls, using standard packing materials and methods. One 20' FCL container can hold 10 metric tons. Payment terms: L/C at sight or T/T.
SPECIFICATIONS OF DIPPED STD POLYESTER TYRE CORD FABRIC NO. | ITEMS | UNITE | 1000
D/2 | 1300
D/2 | 1000
D/3 | 1500
D/2 | 2000
D/2 | 1300
D/3 | 1500
D/3 | 1100 dtex/2 | 1440 dtex/2 | 1100 dtex/3 | 1670 dtex/2 | 2200 dtex/2 | 1440 dtex/3 | 1670 dtex/3 | 1 | Breaking
Stength
(min) ，≥ | N/end | 140 | 180 | 205 | 205 | 280 | 260 | 305 | 2 | Elongation
at | % | 4.5 ± 1.0 44.1N | 4.5 ± 1.0 58.0N | 4.5 ± 1.0 66.6N | 4.5 ± 1.0 66.6N | 4.5 ± 1.0 88.2N | 4.5 ± 1.0 88.2N | 4.5 ± 1.0 100N | 3 | Adhension
(H-test)
(min) ，≥ | N/Cm | 125 | 135 | 140 | 140 | 165 | 165 | 170 | 4 | Breaking
strength difference
(max) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 5 | Breaking elongation difference
(max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 6 | Dip pick up | % | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 3.0 ± 1 | 3.0 ± 1 | 3.0 ± 1 | 7 | Breaking elongation | % | 16 ± 2 | 16 ± 2 | 16 ± 2 | 16 ± 2 | 16 ± 2 | 16 ± 2 | 16 ± 2 | 8 | Diameter | mm | 0.56 ± 0.03 | 0.61 ± 0.03 | 0.66 ± 0.03 | 0.66 ± 0.03 | 0.75 ± 0.04 | 0.74 ± 0.04 | 0.81 ± 0.05 | 9 | Twist | Single twist
(Z) | T/ 10cm | 45 ± 1.5 | 40 ± 1.5 | 37 ± 1.5 | 37 ± 1.5 | 33 ± 1.5 | 33 ± 1.5 | 33 ± 1.5 | Ply twist
(S) | 45 ± 1.5 | 40 ± 1.5 | 37 ± 1.5 | 37 ± 1.5 | 33 ± 1.5 | 33 ± 1.5 | 33 ± 1.5 | 10 | Hot air shrinkage
177 ℃ ×2min x 0.05CN/dtex (max) | % | 3 | 3 | 3 | 3 | 3 | 3 | 3 | 11 | Elongation @ Breaking
of weft yarn (Min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 |
SPECIFICATIONS OF DIPPED HMLS POLYESTER TIRE CORD FABRIC
NO. | ITEMS | UNITE | 1000
D/2 | 1300
D/2 | 1000
D/3 | 1500
D/2 | 2000
D/2 | 1300
D/3 | 1500
D/3 | 1100 dtex/2 | 1440 dtex/2 | 1100 dtex/3 | 1670 dtex/2 | 2200 dtex/2 | 1440 dtex/3 | 1670 dtex/3 | 1 | Breaking
Stength
(min) | N/end | 140 | 180 | 205 | 205 | 270 | 260 | 305 | 2 | Elongation
at | % | 4.5 ± 1.0 44.1N | 4.5 ± 1.0 58.0N | 4.5 ± 1.0 66.6N | 4.5 ± 1.0 66.6N | 4.5 ± 1.0 88.2N | 4.5 ± 1.0 88.2N | 4.5 ± 1.0 100N | 3 | Adhension
(H-test)
(min) | N/Cm | 125 | 135 | 140 | 140 | 165 | 165 | 170 | 4 | Breaking strength difference
(max) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 5 | Breaking elongation difference
(max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | 6 | Dip pick up | % | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 3.5 ± 1 | 7 | Breaking elongation (min) , ≥ | % | 15 ± 2 | 14 | 14 | 14 | 14 | 14 | 14 | 8 | Diameter | mm | 0.56 ± 0.03 | 0.61 ± 0.03 | 0.66 ± 0.03 | 0.66 ± 0.03 | 0.75 ± 0.04 | 0.74 ± 0.04 | 0.81 ± 0.05 | 9 | Twist | Single twist
(Z) | T/ 10cm | 45 ± 1.5 | 40 ± 1.5 | 37 ± 1.5 | 37 ± 1.5 | 33 ± 1.5 | 33 ± 1.5 | 30 ± 1.5 | Ply twist
(S) | 45 ± 1.5 | 40 ± 1.5 | 37 ± 1.5 | 37 ± 1.5 | 33 ± 1.5 | 33 ± 1.5 | 30 ± 1.5 | 10 | Hot air shrinkage
177 ℃ ×2min x
0.05CN/dtex (max) | % | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 11 | Elongation @
Breaking of
weft yarn (Min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 |
Note: All the above products can be produced according to customers' requirements. |
|
|
|