x | Brief introduction Nylon 6 grey and dipped tyre cord fabrics having high strength, fatigue resistance, impact resistance, high adhesion characteristics, are mainly used as reinforcements of bias tyres: - 1. Dipp
 ed tyre cord fabrics that made of multifid yarns are widely used to make auto tyres, agricultural machinery tyres and safety products such as air bags. - 2. Dipped tyre cord fabrics that made of single twisting yarns are widely used to make motorcycle tyres, electric car tyres, bicycle tyres, and other moped tyres.
Specification: We can offer nylon tyre cord fabrics such as 840D/1, 840D/2, 1260D/1, 1260D/2, 1260D/3, 1680D/1, 1680D/2, 1890D/2, etc. Packing: Packed in rolls, using standard packing materials and methods. One 20' FCL container can hold 10 matric tons. Payment terms: L/C at sight or T/T.
Specifications of Single Nylon Tyre Cord Fabric NO. | ITEMS | Unit | 930dtex1
(840D/1) | 1400dtex1
(1260D/1) | 1870dtex1
(1680D/1) | 1 | Breaking strength | N/end | ≥70 | ≥105 | ≥127 | 2 | Elongation at 44.1N | % | | | 8±1.0 | 3 | Elongation at 33.3N | % | | 7.5±1.0 | | 4 | Elongation at 22.6N | % | 7.5±1.0 | | | 5 | Adhesive strength | N/end | ≥49 | ≥64 | ≥78 | 6 | Diameter | MM | 0.32±0.03 | 0.43±0.03 | 0.50±0.03 | 7 | Twist | T/ 10cm | 21±1.5 | 19±1.5 | 19±1.5 | 8 | Unevenness of breaking strength≤ | % | ≤4.5 | ≤4.5 | ≤4.5 | 9 | Unevenness of breaking elongation≤ | % | ≤6.0 | ≤6.0 | ≤6.0 | 10 | Dip pick-up | % | 4.2±1.2 | 4.2±1.2 | 4.2±1.2 | 11 | Breaking elongation | % | 20±2 | 20±2 | 20±2 | 12 | Percentage of moisture | ≤ | ≤0.8 | ≤0.8 | ≤0.8 | 13 | Dry-hot shrinkage | ≤ | ≤4.0 | ≤4.0 | ≤4.0 |
Specifications of Dipped Nylon-6 Tyre Cord Fabric NO. | ITEMS | UNITE | 840D/1 | 840D/2 | 1260D/2 | 1260D/3 | 1680D/2 | 1890D/2 | 930
dtex/1 | 930
dtex/2 | 1400
dtex/2 | 1400
dtex/3 | 1870
dtex/2 | 2100
dtex/2 | 1 | Breaking Stength (min) | N/end ≥ | 67 | 132 | 205 | 305 | 270 | 305 | 2 | Elongation
at 22.1 N | % | 7.0 ± 1.0 | | | | | | Elongation
at 44.1 N | % | | 8.0 ± 1.0 | | | | | Elongation
at 66.6 N | % | | | 8.5 ± 1.0 | | | | Elongation
at 88.2 N | % | | | | | 8.5 ± 1.0 | | Elongation
at 100 N | % | | | | 9.0 ± 1.0 | | 9.0 ± 1.0 | 3 | Adhesion (H-test) (min) | N/Cm ≥ | 49 | 98 | 117 | 150 | 137 | 150 | 4 | Breaking strength difference (max) | ≤ % | 4 | 4 | 4 | 4 | 4 | 4 | 5 | Breaking elongation difference (max) | ≤ % | 6 | 6 | 6 | 6 | 6 | 6 | 6 | Dip pick up | % | 5.0 ± 1.2 | 4.5 ± 1 | 4.5 ± 1 | 4.5 ± 1 | 4.5 ± 1 | 4.5 ± 1 | 7 | Breaking elongation | % | 20 ± 2 | 22 ± 2 | 23 ± 2 | 23 ± 2 | 23 ± 2 | 23 ± 2 | 8 | Diameter | mm | 0.32 ± 0.03 | 0.55 ± 0.04 | 0.65 ± 0.04 | 0.78 ± 0.04 | 0.75 ± 0.04 | 0.78 ± 0.04 | 9 | Twist Single twist (Z) | T/10cm | 21 ± 1.5 | 46 ± 1.5 | 38 ± 1.5 | 32 ± 1.5 | 33 ± 1.5 | 32 ± 1.5 | Ply twist (S) | | / | 46 ± 1.5 | 38 ± 1.5 | 32 ± 1.5 | 33 ± 1.5 | 32 ± 1.5 | 10 | Hot air shrinkage
150 ℃x30min(max) | ≤ % | 6.0 | 7.0 | 7.0 | 7.0 | 7.0 | 7.0 |
Note: All the above products can be produced according to customers' requirements. |
|
|
|