|  Brief introduction As the important reinforcement of the tyres, made of steel and coated with copper, bead wire can strengthen the tyres. Specification: We can offer bead wire mainly from Ф 0.89mm to Ф 1.65mm. Packing: Packed in reels, and then put on pallets, using standard packing materials and methods. One 20' FCL container can hold 25 metric tons. Payment terms: L/C at sight or T/T.
Specifications of Bead Wire: Specification: Ф0.89 Diameter（mm） | 0.89± 0.02 mm | Breaking Strength（Kg/wire） | ≥115 | Elongation (%) | ≥5% | Torsion (Turns/L=200D) | ≥52 | Straightness (mm/ 3m ) | ≤ 600 mm | Bronze plate composition | Copper (%) | ≥97% | Tin (%) | ≤3.0% | Plating thickness (g/kg) | 0.30-1.35 | Adhesion force (N) | ≥800N | Tensile strength (Mpa) | ≥1850 Mpa | Steel Analysis | C (%) | 0.65-0.90 | Mn (%) | 0.30-0.80 | Si (%) | 0.17-0.37 | P&S (%) | ≤0.030 | Linear Density (g/m) | 4.90±0.1 | Bend on 2.50mm (Min) | 11 |
Specification: Ф0.95 Diameter（mm） | 0.95± 0.02 mm | Breaking Strength（Kg/wire） | ≥136 | Elongation (%) | ≥5% | Torsion (Turns/L=200D) | ≥50 | Straightness (mm/ 3m ) | ≤ 600 mm | Bronze plate composition | Copper (%) | ≥97% | Tin (%) | ≤3.0% | Plating thickness (g/kg) | 0.30-1.35 | Adhesion force (N) | ≥800N | Tensile strength (Mpa) | ≥1850 Mpa | Steel Analysis | C (%) | 0.65-0.90 | Mn (%) | 0.30-0.80 | Si (%) | 0.17-0.37 | P&S (%) | ≤0.030 | Linear Density (g/m) | 5.65±0.2 | Bend on 2.50mm (Min) | 11 |
Specification: Ф0.96 Diameter（mm） | 0.96± 0.02 mm | Appearance Quality | Appearance plating uniform and Qualified | Tensile strength（Mpa） | ≥1850 | Breaking Strength（Kg/wire） | ≥136 | Elongation (%) | ≥5% | Torsion (Turns/L=200D) | ≥50 | Straightness (mm/ 3m ) | ≤ 600 mm | Bronze plate composition | Copper (%) | ≥97% | Tin (%) | ≤3.0% | Plating thickness (g/kg) | 0.30-1.35 | Adhesion force (N) | ≥800N | Tensile strength (Mpa) | ≥1850 Mpa | Steel Analysis | C (%) | 0.65-0.90 | Mn (%) | 0.30-0.80 | Si (%) | 0.17-0.37 | P&S (%) | ≤0.030 | Linear Density (g/m) | 5.68±0.2 | Bend on 2.50mm (Min) | 11 |
Specification: Ф1.0 Diameter（mm） | 1.0± 0.02 mm | Breaking Strength（Kg/wire） | ≥148 | Elongation (%) | ≥5% | Torsion (Turns/L=200D) | ≥52 | Straightness (mm/ 3m ) | ≤ 600 mm | Bronze plate composition | Copper (%) | ≥97% | Tin (%) | ≤3.0% | Plating thickness (g/kg) | 0.30-1.35 | Adhesion force (N) | ≥800N | Tensile strength (Mpa) | ≥1850 Mpa | Steel Analysis | C (%) | 0.65-0.90 | Mn (%) | 0.30-0.80 | Si (%) | 0.17-0.37 | P&S (%) | ≤0.030 | Linear Density (g/m) | 6.20±0.2 | Bend on 2.50mm (Min) | 11 |
Specification: Ф1.65Diameter（mm） | 1.65± 0.03 mm | Breaking Strength（Kg/wire） | ≥375 | Elongation (%) | ≥5% | Torsion (Turns/L=200D) | ≥40 | Straightness (mm/ 3m ) | ≤ 600 mm | Bronze plate composition | Copper (%) | ≥97% | Tin (%) | ≤3.0% | Plating thickness (g/kg) | 0.30-1.35 | Adhesion force (N) | ≥800N | Tensile strength (Mpa) | ≥1770Mpa | Steel Analysis | C (%) | 0.65-0.90 | Mn (%) | 0.30-0.80 | Si (%) | 0.17-0.37 | P&S (%) | ≤0.030 | Linear Density (g/m) | 16.8±0.4 | Bend on 2.50mm (Min) | 10 |
Note: All the above products can be produced according to customers' requirements. |
|
|
|